自動(dòng)焊接設(shè)備在焊接過(guò)程中容易出現(xiàn)哪些問(wèn)題？
來(lái)源：http://m.camtask.com/ 發(fā)布時(shí)間：2021-05-10 瀏覽次數(shù)：0
一、自動(dòng)焊接設(shè)備焊接時(shí)會(huì)產(chǎn)生焊縫夾渣，主要有以下三個(gè)方面的原因造成的：
1、 There are three main reasons for slag inclusion in welding seam when automatic welding equipment is used
1、打底焊后不徹底，致使在快速熱焊時(shí)，未能使根部熔渣完全溢出。
1. After the backing welding is not complete, the root slag can not completely overflow during the rapid hot welding.
2、打底焊清根的方法不當(dāng)，使根部焊道倆側(cè)溝槽過(guò)深，呈現(xiàn)W狀。在快速熱焊時(shí)，流到深槽的熔渣來(lái)不及溢出而形成夾渣。
2. The improper method of backing and root cleaning makes the groove on both sides of root pass too deep and W-shaped. In rapid hot welding, the slag flowing to the deep groove has no time to overflow and form slag inclusion.
3、在仰焊位置收弧過(guò)快也易產(chǎn)生夾渣。
3. In overhead welding position, too fast arc stopping is easy to produce slag inclusion.
二、自動(dòng)焊接設(shè)備焊接過(guò)程中產(chǎn)生氣孔的原因：
2、 The causes of Blowholes in the welding process of automatic welding equipment are as follows
1、蓋面焊時(shí)，熔池過(guò)熱，吸覆大量的周邊空氣。
1. During the cover welding, the molten pool overheats and absorbs a lot of surrounding air.
2、蓋面焊時(shí)，焊條擺動(dòng)幅度太大，熔池保護(hù)不佳。
2. During the cover welding, the swing range of welding rod is too large, and the protection of molten pool is poor.
3、根部間隙過(guò)小，容易產(chǎn)生根部針形氣泡。
3. If the root gap is too small, needle shaped bubbles are easy to form at the root.
4、焊條未在規(guī)定時(shí)間內(nèi)用完或長(zhǎng)時(shí)間暴露在空氣中。
4. The welding rod is not used up or exposed to the air for a long time.
三、焊縫產(chǎn)生裂紋的原因
3、 Causes of weld cracks
1、如果施工地段起伏較大，土墩未及時(shí)墊到位，使管子處在受力狀態(tài)，在焊接收弧點(diǎn),尤其是6點(diǎn)鐘位置易出現(xiàn)應(yīng)力裂紋。
1. If the construction section fluctuates greatly and the soil pier is not padded in place in time, the pipe will be in the stress state, and the stress crack is easy to appear at the welding stop point, especially at the 6 o'clock position.
2、在焊接過(guò)程中，如果早松開(kāi)或撤離對(duì)口器，致使熔池中的鐵水未來(lái)的及凝固好，在焊接收弧出容易產(chǎn)生裂紋。
2. In the welding process, if the aligning device is released or withdrawn early, the molten iron in the molten pool will solidify well in the future, and cracks are easy to occur when the welding arc stops.
3、焊工在仰焊位置采用直接熄弧等不當(dāng)?shù)氖栈》椒ǎ率谷鄢匚刺顫M形成弧坑而出現(xiàn)弧坑裂紋。
3. The welder adopts improper arc stopping methods such as direct arc extinguishing at overhead welding position, which leads to the formation of crater cracks due to the incompleteness of molten pool.
四、自動(dòng)焊接設(shè)備焊接時(shí)內(nèi)凹產(chǎn)生的原因
4、 Causes of concave in automatic welding equipment
1、打底焊時(shí)熔透深度不夠。
1. The penetration depth of backing welding is not enough.
2、焊接電流過(guò)大，熱焊時(shí)在5-7點(diǎn)位置焊速太慢。
2. The welding current is too large, and the welding speed is too slow at 5-7 points during hot welding.